PA6-GF20 FR Using Exolit®

Produktbeschreibung

Clariant’s Exolit^® non-halogenated flame retardants provide environmental friendly and sustainable solutions for products used in a variety of industries. Exolit^® is a phosphorus chemistry based flame retardant and is added to polyamide 6 with 20% glass fibers (PA6-GF20 FR) to create an exceptional flame retardant 3D printer filament for parts to be used in numerous end applications. The reinforcement of the polyamide 6 with 20% glass fibers results in a material with very good mechanical properties and an improved heat deflection temperature.

Benefits

Flame retardant material
Semi-crystalline thermoplastic
High impact strength
High stiffness
Outstanding wear resistance
Very good temperature resistance
Reduced thermo-oxidative degradation
Improved long term heat and stability to ultraviolet and visible light
Improved mechanical properties with the additional of 20% glass reinforcement

Applications*

Functional end use parts
Functional prototypes

*Subject to detailed product specifications.

Color Range
Standard

White
Black
High IR transmission black (Polysynthren Black H)
Grey
Yellow
Purple

ColorWorks® ColorForward® consumer color directions 2019

MADE IN HUMAN - Protect the core (red)
DO NOT DISTURB - ἀταραξία von has fidanken (green blue)

ColorWorks^® ColorForward^® consumer color directions 2020

EYE AM WATCHED - Catch me if you can (orange)

Custom colors available upon request.

Printing Parameters

Print Temperature = 250-280°C
Print Speed = 20-50 mm/s
Bed Adhesion = A polyvinylpyrrolidone (PVP) based glue coated on a glass or carbon fiber surface
Bed Temperature = 80°C
Fan Settings = off to low

Note: parameters are dependent on printer used; Clariant tests were performed on an Ultimaker S5 with an aftermarket enclosure and a 3ntr A4 V2 printer.

Typical Property Values

Property	Typical Values				Units	Test Method	Test Specimen
	black	grey	red^a	natural
MECHANICAL PROPERTIES
Tensile stress at yield, 50 mm/min	93 dry^b 64 cond.^c				MPa	ISO 527	Injection molded
	48 dry 29 cond.		51 dry		MPa	ISO 527	3D printed XY / flat at 255°C
	46 dry -- cond.				MPa	ISO 527	3D printed XZ / on edge at 255°C
	-- dry 9.8 cond.		21 dry		MPa	ISO 527	3D printed ZX / upright at 255°C
Tensile stress at break, 50 mm/min	92 dry 63 cond.		74 dry		MPa	ISO 527	Injection molded
	47 dry 29 cond.		50 dry		MPa	ISO 527	3D printed XY / flat at 255°C
	40 dry 30 cond.				MPa	ISO 527	3D printed XZ / on edge at 255°C
	13 dry -- cond.		21 dry		MPa	ISO 527	3D printed ZX / upright at 255°C
Tensile elongation at yield, 50 mm/min	2.8 dry 6.5 cond.				%	ISO 527	Injection molded
	3.6 dry 9.8 cond.		3.7 dry		%	ISO 527	3D printed XY / flat at 255°C
	3.1 dry -- cond.				%	ISO 527	3D printed XZ / flat at 255°C
	-- dry 3.7 cond.				%	ISO 527	3D printed ZX / flat at 255°C
Tensile elongation at break, 50 mm/min	3.3 dry 9.2 cond.		4.4 dry		%	ISO 527	Injection molded
	3.3 dry 10 cond.		3.9 dry		%	ISO 527	3D printed XY / flat at 255°C
	2.7 dry 7.8 cond.				%	ISO 527	3D printed XZ / on edge at 255°C
	1.1 dry 3.1 cond.		1.0 dry		%	ISO 527	3D printed ZX / upright at 255°C
Tensile modulus (modulus of elasticity), 1 mm/min	7278 dry 4793 cond.				MPa	ISO 527	Injection molded
	3761 dry 1725 cond.		4594 dry		MPa	ISO 527	3D printed XY / flat at 255°C
	4077 dry 1922 cond.				MPa	ISO 527	3D printed XZ / on edge at 255°C
	1828 dry 1077 cond.		2648 dry		MPa	ISO 527	3D printed ZX / upright at 255°C
Flexural modulus	6873 dry		5110 dry		MPa	ISO 178	Injection molded
Flexural strength	149 dry		120 dry		MPa	ISO 178	Injection molded
Izod impact notched			7 dry		kJ/m²	ISO 180	Injection molded
Charpy impact notched	2.5 dry		6 dry		kJ/m²	ISO 179	Injection molded
	4.4 dry				kJ/m²	ISO 179	3D printed XY / flat at 255°C
Charpy impact unnotched	29 dry				kJ/m²	ISO 179	Injection molded
					kJ/m²	ISO 179	3D printed XY / flat at 255°C
FLAMMABILITY PROPERTIES
UL 94 flammability rating	V-0 at 0.4 mm					IEC 60695-11-10	3D printed XY / flat at 255°C
	V-0 at 0.8 mm	V-0 at 0.8 mm	V-0 at 0.8 mm			IEC 60695-11-10	Injection molded
	V-0 at 0.8 mm		V-0 at 0.8 mm			IEC 60695-11-10	3D printed XY / flat at 255°C
	V-0 at 1.6 mm	V-0 at 1.6 mm	V-0 at 1.6 mm			IEC 60695-11-10	Injection molded
	V-0 at 1.6 mm		V-0 at 1.6 mm			IEC 60695-11-10	3D printed XY / flat at 255°C
	V-0 at 3.2 mm	V-0 at 3.2 mm	V-0 at 3.2 mm			IEC 60695-11-10	Injection molded
	V-0 at 3.2 mm		V-0 at 3.2 mm			IEC 60695-11-10	3D printed XY / flat at 255°C
Glow Wire Flammability Index (3.0 mm)	960				°C	IEC 60695 2-12	Injection molded
Glow Wire Flammability Index (3.0 mm)					°C	IEC 60695 2-12	3D printed XY / flat at 255°C
Glow Wire Flammability Index (2.0 mm)			960		°C	IEC 60695 2-12	3D printed XY / flat at 255°C
Glow Wire Flammability Index (1.5 mm)	960				°C	IEC 60695 2-12	Injection molded
Glow Wire Flammability Index (1.5 mm)	960		960		°C	IEC 60695 2-12	3D printed XY / flat at 255°C
Glow Wire Flammability Index (0.75 mm)	960				°C	IEC 60695 2-12	Injection molded
Glow Wire Flammability Index (0.75 mm)	960				°C	IEC 60695 2-12	3D printed XY / flat at 255°C
Glow Wire Ignition Temperature (3.0 mm)	775				°C	IEC 60695 2-13	Injection molded
Glow Wire Ignition Temperature (3.0 mm)					°C	IEC 60695 2-13	3D printed XY / flat at 255°C
Glow Wire Ignition Temperature (1.5 mm)	775				°C	IEC 60695 2-13	Injection molded
Glow Wire Ignition Temperature (1.5 mm)	750				°C	IEC 60695 2-13	3D printed XY / flat at 255°C
Glow Wire Ignition Temperature (0.75 mm)	775				°C	IEC 60695 2-13	Injection molded
Glow Wire Ignition Temperature (0.75 mm)	750				°C	IEC 60695 2-13	3D printed XY / flat at 255°C
THERMAL PROPERTIES
Melting point	222 dry	220 dry	220 dry	222 dry	°C	ISO 11357, DSC^d
Glass transition temperature					°C	ISO 11357, DSC
Heat deflection temperature at 1.8 MPa (A)	187 dry		193 dry		°C	ISO 75	Injection molded
	154 dry 142 cond.		136 dry		°C	ISO 75	3D printed XY / flat at 255°C
Heat deflection temperature at 0.45 MPa (B)	206 dry		207 dry		°C	ISO 75	Injection molded
	194 dry 191 cond.		191 dry		°C	ISO 75	3D printed XY / flat at 255°C
GENERAL PROPERTIES
Density	1310	1307	1332	1321	kg/m³	ISO 1183
pH	4.6	4.7					1% in H₂O
Water absorption	3.5		2.9	4.4	%	ISO 62	24 hours at 23°C
Water content - coulometric Karl Fischer					μg/g	ISO 12937
Water content			0.09	0.12	%	ISO 15512	after drying at 120°C for 2 hours
non-volatile-matter content					%	ISO 3251

^a. Organic based color. ^b. Dried at 80°C for 8 hours. ^c. Conditioned at 70% humidity and 25°C. ^d. DSC = Differential Scanning Calorimetry at 10°C/minute.

Note: results are generated according to the valid testing standards indicated above and the standard operating procedures used by the testing facilities.

Packaging and Handling

Delivery Form
1.75 mm and 2.85 mm diameter 3D printer filament.

Packaging
1 kg and 5 kg spools of 3D printer filament. Custom sizes are available upon request.

Storage
Ideally store the 3D printer filament in a cool, dry place at temperatures between 5 to 25°C in a sealed container with the provided Clariant Desi Pak^® desiccant bag. If the 3D printer filament has been exposed to moisture, please dry at 80°C for 3-4 hours with a vacuum or desiccant drying system if possible. Minimum shelf life is 1 year from the date of shipping when properly stored.