PA6/66-GF20 FR Using Exolit®

Typical Property Values

Property	Typical Values				Units	Test Method	Test Specimen
	white	black	reda	natural
MECHANICAL PROPERTIES
Tensile stress at yield, 50 mm/min	80 dry 47 cond.b		87 dry		MPa	ISO 527	Injection molded
		53 dry	-- dry		MPa	ISO 527	3D printed XY / flat at 235°C
			-- dry		MPa	ISO 527	3D printed XZ / on edge at 235°C
		15 dry	-- dry		MPa	ISO 527	3D printed ZX / upright at 235°C
Tensile stress at break, 50 mm/min	78 dry 46 cond.	94 dry	87 dry		MPa	ISO 527	Injection molded
		54 dry	31 dry		MPa	ISO 527	3D printed XY / flat at 235°C
			48 dry		MPa	ISO 527	3D printed XZ / on edge at 235°C
		15 dry	20 dry		MPa	ISO 527	3D printed ZX / upright at 235°C
Tensile elongation at yield, 50 mm/min	2.9 dry 11 cond.		4.0 dry		%	ISO 527	Injection molded
		3.7 dry	-- dry		%	ISO 527	3D printed XY / flat at 235°C
			-- dry		%	ISO 527	3D printed XZ / on edge at 255°C
		0.8 dry	-- dry		%	ISO 527	3D printed ZX / upright at 235°C
Tensile elongation at break, 50 mm/min	4.3 dry 15 cond.		5.6 dry		%	ISO 527	Injection molded
		2.3 dry	5.3 dry		%	ISO 527	3D printed XY / flat at 235°C
			2.0 dry		%	ISO 527	3D printed XZ / on edge at 235°C
		0.8 dry	5.8 dry		%	ISO 527	3D printed ZX / upright at 235°C
Tensile modulus (modulus of elasticity), 1 mm/min	6968 dry 3167 cond.		6883 dry		MPa	ISO 527	Injection molded
		4963 dry	2084 dry		MPa	ISO 527	3D printed XY / flat at 235-240°C
					MPa	ISO 527	3D printed XZ / on edge at 235°C
		1714 dry	1104 dry		MPa	ISO 527	3D printed ZX / upright at 235°C
Flexural modulus	4006 dry	6410 dry			MPa	ISO 178	Injection molded
					MPa	ISO 178	3D printed XY / flat at 235°C
Flexural strength	129 dry	145 dry			MPa	ISO 178	Injection molded
					MPa	ISO 178	3D printed XY / flat at 235°C
Izod impact notched		12 dry			kJ/m2	ISO 180	Injection molded
Charpy impact notched		12 dry			kJ/m2	ISO 179	Injection molded
					kJ/m2	ISO 179	3D printed XY / flat at 235°C
Charpy impact unnotched	33 dry				kJ/m2	ISO 179	Injection molded
					kJ/m2	ISO 179	3D printed XY / flat at 235°C
FLAMMABILITY PROPERTIES
UL 94 flammability rating		V-0 at 0.4 mm				IEC 60695-11-10	3D printed XY / flat at 235°C
		V-0 at 0.8 mm				IEC 60695-11-10	Injection molded
		V-0 at 0.8 mm				IEC 60695-11-10	3D printed XY / flat at 235°C
		V-0 at 1.6 mm				IEC 60695-11-10	Injection molded
		V-0 at 3.2 mm				IEC 60695-11-10	Injection molded
THERMAL PROPERTIES
Melting point		192 dry				ISO 11357, DSCc
Glass transition temperature					°C	ISO 11357, DSC
Heat deflection temperature at 1.8 MPa (A)		160 dry			°C	ISO 75	Injection molded
		125 dry			°C	ISO 75	3D printed XY / flat at 235°C
Heat deflection temperature at 0.45 MPa (B)		188 dry			°C	ISO 75	Injection molded
		173 dry			°C	ISO 75	3D printed XY / flat at 235°C
GENERAL PROPERTIES
Density		1328			kg/m3	ISO 1183
pH							1% in H2O
Water absorption		4			%	ISO 62	24 hours at 23°C
Water content - coulometric Karl Fischer					μg/g	ISO 12937
Water content		0.12			%	ISO 15512	after drying at 120°C for 2 hours
non-volatile-matter content					%	ISO 3251

Packaging and Handling

Delivery Form
1.75 mm and 2.85 mm diameter 3D printer filament.

Packaging
1 kg and 5 kg spools of 3D printer filament. Custom sizes are available upon request.

Storage
Ideally store the 3D printer filament in a cool, dry place at temperatures between 5 to 25°C in a sealed container with the provided Clariant Desi Pak® desiccant bag. If the 3D printer filament has been exposed to moisture, please dry at 80°C for 3-4 hours with a vacuum or desiccant drying system if possible. Minimum shelf life is 1 year from the date of shipping when properly stored.