PA6/66-GF20 FR Using Exolit®

Product Description

Clariant’s Exolit^® non-halogenated flame retardants provide environmental friendly and sustainable solutions for products used in a variety of industries. Clariant's flame retardant 20% glass fiber reinforced polyamide 6/66 using Exolit^® (PA6/66-GF20 FR) 3D printer filament is an exceptionally printing material that has good mechanical properties and achieves UL 94 V-0 flammability standards.

优点

Flame retardant material
Semi-crystalline thermoplastic
Good impact strength and stiffness
Outstanding wear resistance
Good temperature resistance
Reduced thermo-oxidative degradation
Improved long term heat and stability to ultraviolet and visible light

Applications*

Functional end use parts
Functional prototypes

*Subject to detailed product specifications.

Color Range
Standard

White
Black
Grey
Red

ColorWorks^® ColorForward^® consumer color directions 2019

MADE IN HUMAN - Protect the core (red)
DO NOT DISTURB - ἀταραξία von has fidanken (green blue)

ColorWorks^® ColorForward^® consumer color directions 2020

EYE AM WATCHED - Catch me if you can (orange)

Custom colors available upon request.

Printing Parameters

Print Temperature = 230-250°C
Print Speed = 20-50 mm/s
Bed Adhesion = A polyvinylpyrrolidone (PVP) based glue coated on a glass or carbon fiber surface
Bed Temperature = 80°C
Fan Settings = off to low

Note: parameters are dependent on printer used; Clariant tests were performed on Ultimaker S5 and 3ntr A4 V3 printers.

Typical Property Values

Property	Typical Values				Units	Test Method	Test Specimen
	white	black	red^a	natural
MECHANICAL PROPERTIES
Tensile stress at yield, 50 mm/min	80 dry 47 cond.^b		87 dry		MPa	ISO 527	Injection molded
		53 dry	-- dry		MPa	ISO 527	3D printed XY / flat at 235°C
			-- dry		MPa	ISO 527	3D printed XZ / on edge at 235°C
		15 dry	-- dry		MPa	ISO 527	3D printed ZX / upright at 235°C
Tensile stress at break, 50 mm/min	78 dry 46 cond.	94 dry	87 dry		MPa	ISO 527	Injection molded
		54 dry	31 dry		MPa	ISO 527	3D printed XY / flat at 235°C
			48 dry		MPa	ISO 527	3D printed XZ / on edge at 235°C
		15 dry	20 dry		MPa	ISO 527	3D printed ZX / upright at 235°C
Tensile elongation at yield, 50 mm/min	2.9 dry 11 cond.		4.0 dry		%	ISO 527	Injection molded
		3.7 dry	-- dry		%	ISO 527	3D printed XY / flat at 235°C
			-- dry		%	ISO 527	3D printed XZ / on edge at 255°C
		0.8 dry	-- dry		%	ISO 527	3D printed ZX / upright at 235°C
Tensile elongation at break, 50 mm/min	4.3 dry 15 cond.		5.6 dry		%	ISO 527	Injection molded
		2.3 dry	5.3 dry		%	ISO 527	3D printed XY / flat at 235°C
			2.0 dry		%	ISO 527	3D printed XZ / on edge at 235°C
		0.8 dry	5.8 dry		%	ISO 527	3D printed ZX / upright at 235°C
Tensile modulus (modulus of elasticity), 1 mm/min	6968 dry 3167 cond.		6883 dry		MPa	ISO 527	Injection molded
		4963 dry	2084 dry		MPa	ISO 527	3D printed XY / flat at 235-240°C
					MPa	ISO 527	3D printed XZ / on edge at 235°C
		1714 dry	1104 dry		MPa	ISO 527	3D printed ZX / upright at 235°C
Flexural modulus	4006 dry	6410 dry			MPa	ISO 178	Injection molded
					MPa	ISO 178	3D printed XY / flat at 235°C
Flexural strength	129 dry	145 dry			MPa	ISO 178	Injection molded
					MPa	ISO 178	3D printed XY / flat at 235°C
Izod impact notched		12 dry			kJ/m²	ISO 180	Injection molded
Charpy impact notched		12 dry			kJ/m²	ISO 179	Injection molded
					kJ/m²	ISO 179	3D printed XY / flat at 235°C
Charpy impact unnotched	33 dry				kJ/m²	ISO 179	Injection molded
					kJ/m²	ISO 179	3D printed XY / flat at 235°C
FLAMMABILITY PROPERTIES
UL 94 flammability rating		V-0 at 0.4 mm				IEC 60695-11-10	3D printed XY / flat at 235°C
		V-0 at 0.8 mm				IEC 60695-11-10	Injection molded
		V-0 at 0.8 mm				IEC 60695-11-10	3D printed XY / flat at 235°C
		V-0 at 1.6 mm				IEC 60695-11-10	Injection molded
		V-0 at 3.2 mm				IEC 60695-11-10	Injection molded
THERMAL PROPERTIES
Melting point		192 dry				ISO 11357, DSC^c
Glass transition temperature					°C	ISO 11357, DSC
Heat deflection temperature at 1.8 MPa (A)		160 dry			°C	ISO 75	Injection molded
		125 dry			°C	ISO 75	3D printed XY / flat at 235°C
Heat deflection temperature at 0.45 MPa (B)		188 dry			°C	ISO 75	Injection molded
		173 dry			°C	ISO 75	3D printed XY / flat at 235°C
GENERAL PROPERTIES
Density		1328			kg/m³	ISO 1183
pH							1% in H₂O
Water absorption		4			%	ISO 62	24 hours at 23°C
Water content - coulometric Karl Fischer					μg/g	ISO 12937
Water content		0.12			%	ISO 15512	after drying at 120°C for 2 hours
non-volatile-matter content					%	ISO 3251

^a. Organic based color. ^b. Conditioned at 70% humidity and 25°C. ^c. DSC = Differential Scanning Calorimetry at 10°C/minute.

Note: results are generated according to the valid testing standards indicated above and the standard operating procedures used by the testing facilities.

Packaging and Handling

Delivery Form
1.75 mm and 2.85 mm diameter 3D printer filament.

Packaging
1 kg and 5 kg spools of 3D printer filament. Custom sizes are available upon request.

Storage
Ideally store the 3D printer filament in a cool, dry place at temperatures between 5 to 25°C in a sealed container with the provided Clariant Desi Pak® desiccant bag. If the 3D printer filament has been exposed to moisture, please dry at 80°C for 3-4 hours with a vacuum or desiccant drying system if possible. Minimum shelf life is 1 year from the date of shipping when properly stored.