PLA-HI-GF10
3D printer filament

PLA-HI-GF10

3D printer filament

版本编号 :
20190901
版本日期 :
2019年09月01日

Clariant developed this 3D printer filament while testing a number of candidate materials for an industrial customer. The customer desired a very strong and tough (not brittle) material that printed with many common 3D printers and would not regularly require drying. Clariant's high impact modified 10% glass fiber reinforced polylactic acid (PLA-HI-GF10) 3D printer filament proved to be the best material for this industrial customer and is now offered as an exceptional material for the production of manufacturing aids and functional parts that require high strength and toughness. Clariant Hostanox® P-EPQ® and Hostavin® ARO 8 are added to PLA-HI-GF10 to improve the heat stability and resistance to thermo-oxidative degradation and yellowing of the material during printing and usage.

优点
  • Semi-crystalline thermoplastic polyester
  • Easy to print
  • No odour during printing
  • Very high tensile strength (70 MPa 3D printed in XZ direction)
  • High impact strength
  • Reduced thermo-oxidative degradation
  • Minimized undesired yellowing due to ultraviolet light

Applications*
  • Manufacturing aids (jigs and fixtures) for industries such as automotive, aerospace, consumer goods, electrical & electronics, packaging and more
  • Functional parts requiring strength and toughness
  • Prototypes
*Subject to detailed product specifications.

Color Range
Standard
  • White
  • Black
  • Red
  • Fluorescent orange
  • Yellow
  • Green
  • Blue

ColorWorks® ColorForward® consumer color directions 2020

  • EYE AM WATCHED - Catch me if you can (orange)
  • Print Temperature = 200-220°C
  • Print Speed = 30-50 mm/s
  • Bed Adhesion = directly on glass or carbon; a thin coating of ethylene vinyl acetate (EVA) or polyvinylpyrrolidone (PVP) glue may be applied to the bed to further enhance adhesion
  • Bed Temperature = ideally heated up to 60°C
  • Fan Settings = medium to high
  • Heat stability = the heat deflection temperature of the 3D printed part(s) may be increased by annealing the part(s) at 80-130°C (please contact for details)

Notes: parameters are dependent on printer used; Clariant tests were performed on an Ultimaker S5 printer.

Property Typical ValuesUnitsTest MethodTest Specimen
  white blackblueanatural    
MECHANICAL PROPERTIES  
    
Tensile stress at yield, 50 mm/min84 76 MPaISO 527Injection molded
  ---- MPaISO 5273D printed XY / flat at 220°C
  ---- MPaISO 5273D printed XZ / on edge at 220°C
  ---- MPaISO 5273D printed ZX / upright at 220°C
Tensile stress at break, 50 mm/min849876 MPaISO 527Injection molded
  6765 MPaISO 5273D printed XY / flat at 220°C
  8170 MPaISO 5273D printed XZ / on edge at 220°C
  3230 MPaISO 5273D printed ZX / upright at 220°C
Tensile elongation at yield, 50 mm/min2.6
2.4 %ISO 527Injection molded

 ---- %ISO 5273D printed XY / flat at 220°C
  ---- %ISO 5273D printed XZ / on edge at 220°C
  ---- %ISO 5273D printed ZX / upright at 220°C
Tensile elongation at break, 50 mm/min2.72.12.5 %ISO 527Injection molded
  1.52.0 %ISO 5273D printed XY / flat at 220°C
  1.61.9 %ISO 5273D printed XZ / on edge at 220°C
  1.61.0 %ISO 5273D printed ZX / upright at 220°C
Tensile modulus (modulus of elasticity), 1 mm/min634968805135 MPaISO 527Injection molded

 55655094 MPaISO 5273D printed XY / flat at 220°C
  59755193 MPaISO 5273D printed XZ / on edge at 220°C
 
33612864 MPaISO 5273D printed ZX / upright at 220°C
Flexural modulus 

 MPaISO 178Injection molded
Flexural strength 

 MPaISO 178Injection molded
Izod impact notched 

 kJ/m2ISO 180Injection molded
Charpy impact notched5.94.2
 kJ/m2ISO 179 Injection molded
 


 kJ/m2ISO 1793D printed XY / flat at 220°C 
Charpy impact unnotched3030  kJ/m2ISO 179 Injection molded
  2124 kJ/m2ISO 1793D printed XY / flat at 220°C
THERMAL PROPERTIES       
Melting point
175175-178174-175°CISO 11357, DSCb 
Glass transition temperature
606758-62°CISO 11357, DSCb 
Heat deflection temperature at 1.8 MPa (A)104112  °CISO 75Injection molded
 
91
 °CISO 753D printed XY / flat at 220°C
Heat deflection temperature at 0.45 MPa (B)135148 
°CISO 75Injection molded
 
144
 °CISO 753D printed XY / flat at 220°C
GENERAL PROPERTIES       
Density 13191298
kg/m3ISO 1183 
pH 5.96.2
  1% in H2O
Water content - coulometric Karl Fischer  2300 μg/gISO 12937 
Water content - coulometric Karl Fischer  70 μg/gISO 1551260°C for 8 hours in a vacuum oven
non-volatile-matter content ~13~10 %ISO 3251 
a. Organic based color. b. DSC = Differential Scanning Calorimetry at 10°C/minute.

Note: results are generated according to the valid testing standards indicated above and the standard operating procedures used by the testing facilities.

Delivery Form
1.75 mm and 2.85 mm diameter 3D printer filament.

Packaging
1 kg and 5 kg spools of 3D printer filament. Custom sizes are available upon request.

Storage
Ideally store the 3D printer filament in a cool, dry place at temperatures between 5 to 25°C in a sealed container with the provided Clariant Desi Pak® desiccant bag. If the 3D printer filament has been exposed to moisture, please dry at 60°C for at least 8 hours with a vacuum or desiccant drying system if possible. Minimum shelf life is 1 year from the date of shipping when properly stored.
3D Printing
3D Printing
Contact

向科莱恩发送请求

Related products

向科莱恩发送请求

请输入您的联络信息以便我们处理您的请求。感谢您的关注。

3D Printing
3D Printing
Contact
免责声明:
此信息基于我们目前的知识水平,用于对我们产品和可能应用的一般描述。科莱恩不对此信息的准确性、适当性、充分性或无缺陷做出任何明示或默认保证,并且对使用此信息不承担任何相关责任。产品用户有责任确定该产品是否适合特定应用。<br />
<br />
*此信息与科莱恩销售的一般条款和条件无冲突,除非采用书面形式另加说明,否则以一般条款和条件为准。必须遵守所有现有的知识/工业产权。由于我们的产品及其适用的国家/地区和国际法律法规可能变化,我们的产品状态也可能发生改变。处置或存放科莱恩产品时,必须遵循材料安全数据表规定的安全措施,材料安全数据表将按适用法律规定和用户要求提供。在处置这些产品前,您应当获取并浏览适用的材料安全数据表信息。了解更多信息,请联系科莱恩。<br />
<br />
*此外,以下限制适用于美国和加拿大境内的客户:对任何产品或服务的适销性、适合性、特定用途适用性和其他,不作任何明示或默认保证。<br />
<br />
© 科莱恩已在许多国家/地区注册商标。<br />
® 2019 年科莱恩国际有限公司版权所有 

您即将离开 Clariant.com 页面

您点击的链接将在 10 秒内带您离开 Clariant.com 网站页面。 若想停止此操作,单击“取消”。