Licolub® H 12 fine grain
Oxidized, high density polyethylene wax
Important areas of applications are pipe and profile extrusion and extrusion blow molding, especially when the final product does not require high transparency. Also used as an efficiend lubricant in PO based Wood Plastic Composites.
- Accelerates gelation in PVC melts
- Provides excellent anti-sticking properties
- Effective release agent for a variety of polymers
- Efficient lubricant in Wood Plastic Composites
The product does not require a hazard warning label according CLP regulation (Regulation (EC) No. 1272/2008, as amended).
For further information please refer to the Material Safety Data Sheet.
SpecificationsDelivery Specifications and (*) General Properties
|Characteristics||Unit||Target value||Test method|
|Appearance||almost white fine grain||QM-AA-634|
|Acid value||[mg KOH/g]||15 - 19||ISO 2114|
|Drop point||[°C]||100 - 108||ISO 2176|
|Density (23°C)||[g/cm³]||0.94 - 0.96||ISO 1183|
|*Viscosity||[mPa·s]||~ 350||DIN 53019 at 120°C|
ApplicationsOxidired polyethylene waxes for dispersions used in polish, textile, citrus fruit coating, leather and paper applications.
Lubricant for wood plastic composite and especially for rigid and flexible PVC. Licolub H 12 fine grain accelerates gelation and provides excellent anti-sticking properties to the PVC melt.
It can be used as a polar dispersing agent in masterbatch applications and is an effective release agent for polyester, polyurethane, thermosets and rubber.
Packaging and HandlingDelivery form
Polyethylene bag 20 kg
Pallet 1000 kg (50 bags)
BigBag 450 kg
For best shelf life, store this product in a dry area at normal ambient temperatures.
Minimum shelf life is two years form the date of shipping when properly stored.